Arkifloor TX-2000


Arkifloor TX 2000 is a high performance three components, self-smoothing epoxy floor coating system. Designed specially for impact and chemical resistance, with the ease of application on horizontal surfaces. It comprises high grade epoxy resins, hardener as curing agent and selected fine aggregates with colorfast pigments. It gives a smooth, uniform yet hard coating to keep your indoor environment dust-free and hygienic. As a heavy duty coating product, it is an excellent system for old or new _ concrete and cementitious floor of industrial or commercial laboratories, food factories, manufacturing factories and warehouses. It is also suitable for use in workshops, power plants, wafer plants, and chemical storage rooms. It comes in a wide range of colors for your flooring needs.

- Self-leveling and dust-proofing capability with seamless finish reduces floor maintenance
- Pre-formulated for use in warm humid environment
- Excellent impact, chemical and abrasion resistance for heavy vehicular movement
- Retards the growth of fungi and mould
- Easy mixing and application at site

Surface Preparation:
Concrete surfaces should be well cured and free from dirt, dust, oil, grease and foreign matters. Any unsound substrates, cracks, and pot-holes should be made good with the appropriate SKK filler product. Concrete is highly susceptible to uprising moisture, which can decrease the effectiveness of any coating system. Installation of a water-proofing membranes is mandatory to prevent glitches in the dynamics of any coating system. Smooth concrete surfaces may have to be chemically cleaned or mechanically scarified to provide bonding keys before the coating can be laid. Etching neutralizes the alkaline surface and provides a better bond. It also helps remove salt deposits or laitance that can occur on concrete surfaces.
Masonry and Mortar Substrate Masonry surfaces may peel due to efflorescence, where soluble salts are present. It is therefore essential to treat the surfaces free from dirt, dust, oil, grease and foreign matters. Environmental determinants like humidity can also cause — structural or superficial cracks with mortar. Restoration work should be carried out to amend these problems prior to the application of paint. If efflorescence is also evident, it must be removed before repainting. Remove all flaking or chalking paint from the damaged area by wire brushing or sandblasting. If surface is very porous, apply SK Floor Filler, an epoxy resin-based cementitious conditioner to mend the surface.

Application Data:
No. of Component: Three
No. of Coat: One - Two

3.80 - 4.30 kg/m2/Coat for 2mm thickness

Mixing Ratio (By weight ratio):
base 5 kg
Hardener 2.2 kg
Aggregate 10 kg

Overcoating Interval: 7 days
Method of Application: By Roller or Trowel

Packing Style:
Base 5 kg/can
Hardener 2.2 kg/can
Aggregate 10 kg/bag